Samarium Cobalt (SmCo) Magnets – Strength & High Temp Use

Samarian Cobalt (SmCo) Magnets

Introduction

An explanation of SmCo magnets and their importance with a list of manufacturers and suppliers

You will learn:

What is a SmCo Magnet?
How SmCo Magnets are Made
Uses for SmCo Magnets
Types of SmCo Magnets
And much more ...

Chapter 1: What is a SmCo Magnet?

SmCo magnets are strong rare earth permanent magnets that are used for a variety of industrial applications. They have two primary phases, which are SmCo₅ and Sm₂Co₁₇. The difference between the phases is in regard to their magnetic energy, temperature resistance, and the number of samarium and cobalt atoms.

SmCo magnets are known for their high magnetic strength with an MGOe range between 16 and 32 MGOe. The term MGOe is a unit measure, Maximum Energy Product, of a magnet. It is indicative of a magnet’s strength and efficiency. Strong powerful magnets have a high MGOe and a strong magnetic field that provides exceptional performance.

SmCo magnets have excellent magnetic stability in high or low temperature conditions. Unlike other types of magnets, SmCo magnets have high resistance to demagnetization and corrosion, without requiring a coating The stability and strength of SmCo magnets has led to their use in high performance motors, sensor systems, and various technical applications.

Although neodymium iron boron magnets are the strongest rare earth magnets, they lose their strength at extremely high temperatures and corrode easily, which necessitates that they be coated with electroplating or epoxy. SmCo magnets can withstand temperatures as high as 260°C (500°F) and are able to resist the effects of corrosion.

SmCo magnets were perfected in the 1960s and introduced to the world in the 1970s. They were the first rare earth magnet. Their introduction revolutionized magnets and replaced aluminum nickel cobalt (Anico) alloy magnets, which was the standard magnet at that time. SmCo magnets replaced Anico alloy magnets due to being three times stronger than Anico magnets.

Chapter 2: How Samarian Cobalt Magnets are Made

Samarian cobalt magnets are rare earth magnets with high magnetic energy and a low temperature coefficient with an operating temperature that can reach as high as 350°C (662°F). When placed in conditions that exceed 180°C (356°F), the magnetic energy product (BHmax), coercivity, temperature stability, and chemical stability of SmCo magnetic exceeds that of NdFeB magnets.

Several manufacturing processes are used to produce SmCo magnets with the two most common being isostatic pressing with the second method being sintering. The differentiation between the methods is the form of SmCo powder that is used for the initial step in the processing. Isostatic pressing begins with SmCo powder that is mixed with a plastic carrier, while sintering involves heating the samarium cobalt powder to near its melting point.

Alloying Samarium and Cobalt

Samarium is a rare earth element that is shiny. It is named after a Russian mine official, Colonel Vasili Samarsky Bykhovets. It comes from samarskite, a complex oxide mineral with concentrations of rare earth elements, uranium, and thorium. Samarskite was first discovered in the Ural Mountains of Russia but has been found all over the world. In its natural state, samarskite is a velvet black mass. Samarium makes up 2.8% of samarskite and other minerals. It is found in China, the United States, Brazil, India, Sri Lanka and Australia, with China being the world leader. Samarium (Sm) is a chemical element with the atomic number of 62.

Cobalt (Co) is referred to as a transition metal that is found naturally with copper and nickel with an atomic number of 27. It is sourced from cobaltite, erythrite, copper, and nickel. It is chosen for the production of magnets due to its high ferromagnetic properties. Cobalt is the part of SmCo magnets that is resistant to corrosion and capable of withstanding extremely high temperatures. Although cobalt is mainly used for battery technology, its strength and temperature resistance has made it valuable for 3D printing and different forms of renewable energy solutions.

To achieve the desired magnetic properties for SmCo magnets, samarium and cobalt are precision proportioned. The alloying process involves melting the metals in an induction furnace that contains argon. The inert properties of argon create a non-reactive environment that prevents contamination to ensure the purity and quality of the materials.

Although argon is expensive, it is used in the alloying process for SmCo magnets to ensure the integrity of the metals. During the process, samarium and cobalt are allowed to synergize to create magnets with exceptional strength and temperature stability, the main characteristics of SmCo magnets. To further enhance SmCo magnets, various alloys are added in small amounts, such as iron, copper, and zirconium. The use of the additional alloys is to alter the characteristics of SmCo magnets to match the requirements of a specific application.

The melted mixture is cast and formed into ingots that will be used for the raw materials to produce SmCo magnets. An essential part of the alloying process is the cooling of the ingots to form a solid metal piece. Various methods are used with water being the most common.

Milling

The milling process involves crushing the ingots to form a fine powder. Of the many steps in the manufacture of SmCo magnets, this aspect of the process is essential. The ingots have to be crushed in such a way that the result is a powder with a uniform particle size. To achieve a properly oriented magnet, the particles in the powder are required to have a size of 3 to 4 micrometers (μm). Concentrated size distribution with particles that are spherical or nearly spherical further assures the success of SmCo magnets.

The alloying, casting, and milling of samarium and cobalt, described above, is the process that is used the most for preparing the raw materials for SmCo magnet production. After this initial stage, the manufacturing of SmCo magnets takes different forms, with bonding or isostatic pressing and sintering being two of the most used.

Bonded or Isostatic Samarium Cobalt Magnets

Bonded or isostatic pressing samarium cobalt magnets are an alternative to sintered samarium cobalt magnets. The alloying process includes the mixing of the powder with a binding agent, such as an epoxy resin, and compressing the mixture into the final shape of the magnet. With the hot press method, the powder is placed under high pressure with heat. Due to the heat, the powder particles fuse to create a solid compact cohesive shape. The application of heat, in the presence of a magnetic field, orients the powder particles.

The use of heat to produce bonded SmCo magnets orients the powder particles, which makes most bonded samarium cobalt magnets anisotropic, where the magnetization is in one direction. This aspect of the bonded samarium cobalt magnets gives them stronger magnetic properties than isotopic magnets. In addition, isostatic compression magnets have close tolerances, eliminating the need for machining, and can be configured into complex shapes.

Other Compaction Methods

The compacting of the powder to form SmCo magnets takes several forms, each having distinguishing characteristics. The method chosen for producing SmCo magnets is dependent on the manufacturer and the type of magnet that is required.

Axial Pressing – With axial pressing, the alloyed powder is placed in the cavity of a tool on a press. An aligning field is applied prior to the implementation of the compaction process. The tool cavity filled with the powder is compressed under great pressure to freeze in the alignment. The aligning field is parallel to the direction of the compaction.
Transverse Pressing – The process for transverse pressing is the same as axial pressing up until the alignment phase where the field is perpendicular to the compaction press. Since the powder particles are elongated in the direction of the magnetic alignment, the magnets have a better alignment and higher energy.

Magnetic field compacting uses the interaction between the powder and magnetic field to align the powder’s magnetization direction to make it consistent with the final magnetization direction. The use of magnetic field orientation is used to produce anisotropic magnets.

Sintered Samarium Cobalt Magnets

The initial steps for the manufacture of sintered samarium cobalt magnets are the same as those for bonded samarium cobalt magnets. The differentiation in the processes is the following steps where additional chemicals are added to the process. The sintering process heats the powder mixture to just below its melting point to bond and form a solid structure.

The set temperature and the presence of a vacuum or inert gas determines the type and grade of SmCo magnet being made. The purpose of the vacuum is to prevent the forming of an oxide film that would lower the quality of the final magnets. During the heating process, the SmCo magnets are heated to a sintering temperature that densifies the mixture. The powder is pressed into a die and is heated to 1250°C (2282°F), which solidifies and fuses the powder. The length of the sintering time affects grain growth and has to be sufficient to achieve proper density.

When the material is at the highest temperature, it is given a solutionizing treatment. At the completion of the sintering, the SmCo magnets are tempered between 700°C and 900°C

(1292°F and 1652°F). After they have cooled, they have their magnetic field applied. During sintering, the magnets shrink, linearly, by 15% to 20% and have a rough surface with no evident magnetic field.

Machining Sintered Samarium Cobalt Magnets

Unlike bonded samarium cobalt magnets, sintered samarium cobalt magnets are ground and finished using a water cooled diamond coated grinding machine. The sintered material is very hard and brittle at Rockwell C57 up to C61, which is the reason for the use of diamond coated grinding tools. The grinding process takes different forms, which can include grinding them smooth and parallel, OD and ID grinding, or slicing the magnet blocks into smaller portions. When the slicing process is performed, with exacting precision, other grinding may not be necessary.

There are several factors that are meticulously controlled during the grinding process to avoid damaging the final SmCo magnets. Care in the process is necessary to avoid chipping and cracking the magnets. When the final shapes are being produced in low volume, electrical discharge machining (EDM) can be used for simple dimensional profiles.

Machined SmCo magnets have sharp edges that chip easily. Since coating is difficult, other measures are taken to remove the sharpness. A common method for high volume magnet production is vibratory tumbling that includes an abrasive media.

SmCo magnets do not require a surface like the coatings that are applied to Neodymium magnets, which can rust and react to chemicals. The mixture of samarium and cobalt is naturally resistant to corrosion. Regardless of this factor, there are occasions when epoxy, electrolytic nickel, and aluminum IVD is applied. Conversion coatings are also used but provide temporary protection.

Magnetizing

At the end of the casting, heating, and machining, the magnets need to be charged to produce a magnetic field. Magnetization aligns the magnetic dipoles, which is achieved by applying a magnetic field or exposing the material to a magnetic field. The strength of the magnetization and magnetic field depends on the type of material and the strength of the applied magnetic field.

The magnet field applied to a SmCo magnet is 2 to 3 times stronger than its coercivity. With high coercivity magnets, magnetization fields may reach as high as 30,000 to 40,000 oersted (Oe), the unit measure of the strength of a magnetic field. During magnetization, the domains of a magnet are aligned permanently in the desired direction and give the magnet its full potential.

Magnetization can be accomplished in a solenoid or with fixtures designed to pass magnetic properties. In most cases, magnetization is completed by a magnetizer that has coil wire with electric current. When a magnetizer is turned on, it discharges a magnetic field that activates the magnetism of a SmCo magnet slug.

Two common forms of magnetization are:

Static – Static magnetic fields are constant and do not change direction over time. The strength of a static magnetic flux is expressed in Tesla (T) or gauss (G).
Pulse – Pulse magnetization is used to create strong magnetic fields, for multipolar magnetization, or for magnetizing materials with high coercivity. The process involves applying a very short pulse current of approximately a microsecond or millisecond long to the magnet material.

Stabilization and Calibration

There are special cases where SmCo magnets will require stabilization and calibration. Stabilization is a treatment to prevent demagnetizing influences that could change the performance of a magnet. Calibration is a treatment that narrows the performance range of a magnet to achieve a tight tolerance for the requirements of an application. Stabilization and calibration ensure that a magnet can perform within a specified temperature and have tight tolerances on flux output.

SmCo magnets provide exceptional performance until they are driven beyond their parameters, which leads to irreversible loss. When loss may come from elevated temperatures, then thermal stabilization is performed. If demagnetization is possible, then magnetic stabilization is performed.

Flux output is an aspect of magnets that is unavoidable. SmCo magnets are known to have a high flux output, the strength of a magnet’s magnetic field. In the majority of cases, flux output has little effect on an application. In special cases, where tight tolerances are required, magnets need to be calibrated to a specific range of temperatures. In those instances, SmCo magnets with pulses per minute (ppm) of less than 50 ppm are used.

Leading Manufacturers and Suppliers

Chapter 3: Grades of Samarium Cobalt Magnets

There is a wide variety of samarium cobalt magnets that are designed to support general and specialized industrial applications. The range of grades extends from 16 MGOe to 32 MGOe. The many types make it possible to optimize cost, performance, and resistance to temperature. The two main types of samarium cobalt magnets are 1-5 and 2-17, which are differentiated by the number of samarium atoms to cobalt atoms.

Samarium Cobalt (1-5) SmCo₅

Samarium cobalt (1-5) is an older version of samarium cobalt magnets. It is designated as 1-5 due to its structure, which is one samarium atom per five cobalt atoms. The energy product of 1-5 ranges between 15 MGOe and 24 MGOe. This form of SmCo magnet can operate in temperatures up to 250°C (482°F) and is 35% samarium and 65% cobalt.

Samarium Cobalt (2-17) Sm₂Co₁₇

Samarium cobalt (2-17) is a newer samarium cobalt magnet material that has two samarium atoms and 14 to 17 cobalt atoms, with the 14-17 atoms being a mix of transition metals that include copper and iron with cobalt being the most abundant. The energy range of 2-17 magnets is between 21 MGOe and 32 MGOe with operating temperatures between 300o C up to 350°C (572°F up to 662°F). Samarium cobalt alloy for 2-17 is 25% samarium and 75% transition metals that are composed mostly of cobalt. The higher energy density and operating temperatures for this magnet alloy makes it an ideal choice for a wide variety of applications.

The main types of samarium cobalt magnets, SmCo₅ and Sm₂Co₁₇, are divided into 11 subgrades with each group given its name in accordance with their ratio of samarium atoms to cobalt atoms. The grades of SmCo magnets are identified by their strength, which range from 16, 18, 20, 22, 24, 26, 28, 30, and 32 MGOe.

When examining a table for magnets, there are letters placed after some grades, which represent a magnets ability to withstand demagnetization, temperature, and other forces that work against a magnet. Each magnet manufacturer has a different system for defining coercive force with the lettering system being the most widely used.

The identifiers for SmCo₅ and Sm₂Co₁₇ grades include three parts. Letter 1, which is a single or set of letters, indicates material type, which is followed by a number that is the (BH) max MGOe level value. The final letter, letter 2, is the Hci level or coercivity level. Sintered SmCo magnets are identified by letter 1 being XG or XGS with XG for SmCo5 and XGS for Sm₂Co₁₇. The letter 2 or Hci levels are identified by default, H, L, M, and LT. An example of a label for a Sm₂Co₁₇ magnet is XGS28H where XGS means sintered, and 28 is the magnets maximum MGOe level with H specifying the Hci or coercivity level.

Samarium Cobalt Materials Chart for SmCo Sintered Magnets
	Grades	Remanence		Coercivity				Max Energy		Max Working Temperature
		Br		HcB		HcJ		(BH)max		TwMax
		T	kGs	kA/m	k0e	kA/m	k0e	kJ/m³	MG0e	°C
Sm₁Co₅	Sm1Co5-20	0.89-0.93	8.9-9.3	684-732	8.6-9.2	≥1830	≥23	151-167	19-21	≤250
	Sm1Co5-22	0.92-0.96	9.2-9.6	710-756	8.9-9.5	≥1830	≥23	159-175	22-24	≤250
	Sm1Co5-24	0.96-1.00	9.6-10.0	740-788	9.3-9.9	≥1830	≥23	175-191	22-24	≤250
Sm₂Co₁₇	Sm2Co17-30L	1.08-1.10	10.8-11.0	541-796	6.8-10.0	636-955	12-Aug	223-239	28-30	≤250
	Sm2Co17-32L	1.10-1.15	11.0-11.5	541-812	6.8-10.2	636-955	12-Aug	231-255	29-32	≤250
	Sm2Co17-30M	1.08-1.10	10.8-11.0	676-835	8.5-10.5	955-1433	18-Dec	223-239	28-30	≤300
	Sm2Co17-32M	1.10-1.15	11.0-11.5	676-852	8.5-10.7	955-1433	18-Dec	231-255	29-32	≤300
	Sm2Co17-28	1.03-1.08	10.3-10.8	756-812	9.5-10.2	≥1433	≥18	207-223	26-28	≤300
	Sm2Co17-30	1.08-1.10	10.8-11.0	788-835	9.9-10.5	≥1433	≥18	223-239	28-30	≤300
	Sm2Co17-32	1.10-1.15	11.0-11.5	812-860	10.2-10.8	≥1433	≥18	231-255	29-32	≤300
	Sm2Co17-28H	1.03-1.08	10.3-10.8	756-812	9.5-10.2	≥1990	≥25	207-223	26-28	≤350
	Sm2Co17-30H	1.08-1.10	10.8-11.0	788-835	9.9-10.5	≥1990	≥25	223-239	28-30	≤350
	Sm2Co17-32H	1.10-1.15	11.0-11.5	812-860	10.2-10.8	≥1990	≥25	231-255	29-32	≤350

A critical factor for all forms of magnets is their temperature rating, which is indicated by one or two letters. When letter or letters are placed after a grade, it is an indication that the magnet has the ability to fight against demagnetization. Since heat is a major factor and most common force that affects magnets, there are certain acceptable general rules to indicate temperature considerations. The letters used are M, H, SH, UH, EH, and TH with M meaning an operating temperature of 100°C (212°F) from which the temperatures progress to TH for 220°C (428°F).

Chapter 4: Types of Samarium Cobalt Magnets

As with all forms of industrial magnets, samarium cobalt magnets are available in different forms. Each of the different shapes are designed for a specific application and purpose. The many shapes of SmCo magnets are common to all forms of magnets with differentiating factors being their strength and magnetic field.

Block

Block magnets are six sided magnets with straight sides that meet at a right angle. Each of the sides are parallel and give the appearance of a block of wood. The wide use of SmCo block magnets is due to their magnetic strength, temperature stability, high coercivity, and exceptional resistance to corrosion. SmCo block magnets are available in a wide assortment of sizes and grades, which can be tailored to meet the needs of a specific application.

SmCo block magnets are used where magnets have to endure high temperatures, such as critical sensors. In addition, they are utilized in speakers, reed switches, motors, rotors, wind turbines, AC/DC motors, drive motors, and servo motors.

Disc

Samarium cobalt disc magnets are flat, circular, coin shaped magnets that are available in varying diameters and thicknesses to meet the specific requirements of an application. The compactness of SmCo magnets makes them ideal for applications that require small magnets but able to endure high temperatures in corrosive environments. SmCo disc magnets are used for coreless motors, variable frequency air conditioners, dewaxing motors for the oil industry, sensors, computer disc drivers, and linear actuators. They are chosen for applications where low-carbon and energy savings are essential.

Pot

Samarium cobalt pot magnets have one exposed surface with a magnetic field that creates concentrated force. The magnet is contained within a housing or casing that is referred to as a shell or pot. The design of pot magnets enhances their magnetic force, a factor that radically influences their attracting power, while protecting the magnet from damage and outside forces.

SmCo pot magnets are widely valued due to their exceptional temperature and corrosion resistance. They are shipped with a keeper plate that protects the magnet during shipping or when they are handled. The ferromagnetic housing of SmCo pot magnets is available in different shapes and designs, which allows them to include threaded bars, tapped threaded holes, countersunk holes for screws, and blind ends for gluing into place. These aspects of SmCo pot magnets differentiates them from the configuration of traditional magnets.

Both compositions of SmCo magnets, SmCo₅ and Sm₂Co₁₇, are used in the manufacture of pot magnets, with Sm₂Co₁₇ having the highest energy product of MGOe 30. The design and strength of SmCo pot magnets has made them a highly valued magnet for industrial use.

Ring

Ring magnets are similar to SmCo disc magnets in that they are round circular magnets. What differentiates them from disc magnets is a hole in the center of the magnet. SmCo ring magnets come in a wide variety of sizes with differing outer diameters (ODs) and inner diameters (IDs), which makes the magnets very versatile and able to be used for a wide range of applications. A common use for ring SmCo ring magnets is in aerospace and medical devices. The fact that SmCo ring magnets do not require a coating is the reason they are chosen for applications in hostile environments.

Cylinder

Cylinder magnets are long, round, circular magnets where their length exceeds their diameter. Often referred to as rod magnets, SmCo cylinder magnets are recessed into drilled holes to provide a strong magnetic field in applications that have limited space. SmCo cylinder magnets have straight parallel sides with a circular or round cross section. Their dimensions are determined by their length or height and diameter, which is also used as a descriptor. The design of rod or cylinder SmCo magnets allows them to generate a strong magnetic field from the small surface of their pole area.

Arc

Samarium cobalt arc magnets are a special form of SmCo magnet that has a curved shape to be used in rotating machinery, like rotors and stators. They are produced in tile form segments in order to align with circular systems and provide focused magnetic force. Known as curved, tile and segment magnets, SmCo arc magnets are a crucial part of magnet motors, generators, and magnetic couplings.

As with all other uses for SmCo magnets, arc magnets are added to applications that endure high temperatures. They supply the type of reliable service required for an application to be successful. SmCo arc magnets are not as widely known as Neodymium arc magnets but have many of the same characteristics as NdFeb magnets. They have similar magnetization directions, machining processes, and geometries that boost equipment performance. Where SmCo arc magnets excel over NdFeb magnets is in hostile conditions with high temperatures and the potential of demagnetization.

Chapter 5: Samarium Cobalt Magnets Compared to Neodymium Magnets

Samarium Cobalt and Neodymium Iron Boron magnets are the most important industrial magnets. Although NdFeb magnets outperform SmCo magnets in many applications, there are characteristics of samarium cobalt magnets that make them superior to Neodymium magnets in certain circumstances.

The similarities between SmCo and NdFeb magnets include their strong magnetic fields with a very high BH Max and exceptional coercivity, resistance to demagnetization. Since their discovery, SmCo and NdFeb magnets have become an essential part of multiple industrial processes.

Samarium Cobalt Magnets Compared to Neodymium Magnets

Corrosion Resistance

A large portion of SmCo magnets is composed of cobalt, about 65%, which is a major part of stainless steel. It makes SmCo magnets highly resistant to corrosion. In contrast, 65% of NdFeb magnets is the ferromagnetic metal iron, which has very limited resistance to corrosion. To improve NdFeb magnets resistance to corrosion, they have a small amount of cobalt added, about 1.5%. In addition, for further protection, they are electroplated or coated. The service life of a NdFeb magnet depends on the quality and effectiveness of its coating.

Temperature Coefficient

SmCo magnets are well known for being able to operate at extreme temperatures, far beyond those that NdFeb magnets can endure. SmCo magnets lose less field strength per degree of temperature increase than NdFeb magnets. This factor makes it easier for engineers to adjust temperature effects since the effects are so small. Temperature is one of the causes for magnets to demagnetize and is an area that SmCo magnets excel.

Magnetic Strength

Of the two magnets, neodymium iron boron magnets are the strongest at room temperature up to 180°C (356°F). Their strength rapidly declines as the temperature rises. After NdFeb magnets reach their optimum performance temperature, SmCo magnets easily outperform them.

Coercivity

Coercivity, resistance to demagnetization, is high for both SmCo and NdFeb magnets compared to other forms of magnets. NdFeb’s vulnerability to high temperatures is the major factor in their use.

Applications

The applications for which neodymium iron boron magnets are used include motors, generators, and miniaturization. Other applications are:

Loudspeakers and Other Electric Acoustic Applications
Automotive EV Drive Motors
Automotive Accessory Motors
Mobile Phones
Sensors
Head Actuators for Computer Hard Disks
Mechanical E-cigarette Firing Switches
Locks for Doors

Mobile Phones
Magnetic Bearings and Couplings
Benchtop NMR Spectrometers
Electric Generators for Wind Turbines
Retail Media Case Decouplers
Catch Foreign Bodies to Protect Products and Processes
Identifying Precious Metals
Pickup Tool

Applications for which samarium cobalt magnets are used include ones with high temperatures and heavy loads. Other applications include:

Railroad Locomotive Traction Motors
Heavy Industrial Motors And Generators
Marine Motors And Generators
Defense-Related Motors
Down Hole Applications in Oil And Gas
High Performance Motors
Actuators
Generators
Turbo Machinery
Electric Motors
Magnetic Separation Devices
Traveling Wave Tubes
Magnetic Couplings
Sputtering Deposition
Magnetic Bearings

Sensor Systems
Drilling Equipment
Wind Turbine Equipment
Energy Recovery Systems
Medical Devices
Missile Components
Industrial Automation Equipment
Pipeline Inspection
Robotic Arms
Gyroscopes
Accelerometers
Particle Accelerators
Magnetic Drive Components
Halbach Arrays

Cost

Neodymium magnets are more affordable than samarium cobalt magnets due to the abundance of their elements. Neodymium, iron, and boron are readily available and inexpensive. Samarium and cobalt are scarce and more costly to acquire. In addition, the manufacturing methods used to produce SmCo magnets is highly technical, complex, and requires a great deal of energy.

Brittleness

The iron content of neodymium magnets makes them stronger and resistant to cracking and braking. Samarium cobalt magnets are brittle and crack or chip easily if handled incorrectly.

Conclusion

Samarium cobalt is part of the lanthanide group on the period table and is a close relative of Neodymium. The two elements are rare earth elements and are used in the manufacture of permanent magnets.
There are two phases of SmCo magnets, which are SmCo₅ and Sm₂Co₁₇. Of the two phases, Sm₂Co₁₇ has the higher magnetic strength and greater temperature resistance.
Samarium cobalt magnets have a magnetic energy product that ranges between 16 MGOe and 32 MGOe. They are the second strongest rare earth magnet after Neodymium magnets.
The methods used to manufacture SmCo magnets are isostatic pressing and sintering. The initial steps of both processes are the same. They differ in how the final products are formed.
Samarium cobalt magnets are rare earth magnets, which are brittle and can crack or chip easily. They must be handled with care to prevent injuries and potential hazards. If samarium magnets collide, they shatter into extremely small particles that are dangerous if swallowed or allowed to rest on the skin.