Here is the most concise information on alumina ceramics on the internet.
You will learn:
Alumina ceramics, renowned for their exceptional hardness, are robust industrial oxide ceramics. These ceramics are derived from bauxite and can be fabricated using various techniques such as injection molding, die pressing, isostatic pressing, slip casting, diamond machining, and extrusion. Their sintered crystalline form resembles that found in sapphire and ruby.
Primarily, alumina ceramics serve as insulating materials for electrical applications. They are highly prized for their incredible strength, as well as their excellent resistance to wear and corrosion.
Products made from alumina ceramics, illustrated in the image below, exhibit resistance to chemicals, high temperatures, wear, erosion, and corrosion. Their bioinert nature also makes them suitable for medical implants.
Alumina ceramics are classified as technical ceramics due to their outstanding properties and the advantageous cost-to-performance ratio. They are categorized based on their alumina content, which varies from 70% to 99.9%. Higher purity alumina components exhibit improved resistance to wear and corrosion.
Alumina ceramics, also known as aluminum oxide ceramics or Al2O3 ceramics, are a crucial class of advanced ceramic materials used across multiple industries for their outstanding mechanical, thermal, and electrical properties. Typically white and granular in appearance, they may resemble table salt or appear as a silky, dense white powder. There are three primary types of alumina: hydrated, calcined, and tabular. Each type is available in various grades and formulations, tailored to specific industrial applications.
The different types of alumina vary based on their content of soda (Na2O), iron (Fe2O3), and silica (SiO2), as well as their chemical purity and the specific properties of the powder used in their production. Selecting the right grade of alumina ceramic is critical for applications in electronics, medical components, cutting tools, wear-resistant parts, and refractory linings, where performance and reliability are essential.
Calcined alumina is produced by heating aluminum oxide to 1050°C (1900°F). This process removes all impurities and water, resulting in a very pure form of alumina with a purity of 99.99%. It achieves a hardness rating of 9 on the Mohs scale, just below the 10 rating of diamonds. Used extensively in high-performance abrasives, precision-engineered components, and electrical insulators, calcined alumina is recognized for its thermal stability, high strength, and resistance to chemical attack.
Hydrated alumina, also known as alumina hydroxide or aluminum hydroxide, is valued for its use in glazes due to its ability to remain suspended in glaze slurries and its adhesive properties. It also acts as a flame retardant, filler material, and a precursor in the Bayer refining process for producing high-purity alumina. Hydrated alumina serves in water treatment, catalyst supports, and specialty ceramics formulations, making it invaluable in both industrial and environmental applications.
Tabular alumina is created by heating aluminum oxide to 1650°C (3000°F). It boasts high thermal capacity, exceptional temperature stability, and excellent strength. This type of alumina is produced by sintering calcined alumina balls, which are then crushed into a powder. Tabular alumina is known for its high refractoriness, mechanical strength, wear resistance, chemical purity, dielectric properties, and resistance to corrosion in both acids and alkalis. These properties make tabular alumina ideal for refractory bricks, kiln furniture, high-temperature furnace linings, and advanced engineered ceramics used in aggressive industrial environments.
Alumina maintains its physical and mechanical properties in both oxidizing and reducing atmospheres up to 1650°C (2900°F) and in vacuum environments up to 2000°C (3600°F). At 1000°C, it retains 50% of its tensile strength compared to room temperature. Unlike metals, which weaken and deform at high temperatures, alumina ceramics preserve their strength and remain structurally stable when temperatures return to normal. This superior heat resistance makes alumina ideal for applications such as furnace linings, thermal insulation, and crucibles where extreme temperatures are typical in industries like metallurgy, glass manufacturing, and semiconductor processing.
Abrasion occurs when a material is worn down through friction and rubbing. The ability of a material to resist abrasion means it maintains its original structure even after enduring mechanical wear. Alumina ceramics exhibit high abrasion resistance due to their inherent hardness. This property is especially valued in industrial sectors such as mining, power generation, and materials processing, where alumina is used for wear liners, pump seals, valves, and cutting tools, drastically improving the lifespan and durability of equipment compared to traditional metals or plastics.
Alumina demonstrates excellent resistance to both acids and alkalis at high temperatures because it is chemically inert. This lack of chemical reactivity makes it resistant to the effects of various chemicals, including solvents, salt solutions, and aggressive industrial reagents. As a result, alumina ceramics are widely used in chemical processing industries, laboratory wares, semiconductor fabrication, and biomedical devices where corrosion resistance and purity are paramount.
Density refers to a material's mass divided by its volume, typically expressed in grams per cubic centimeter (g/cmÂł). In this context, mass is measured in grams and volume in cubic centimeters. The density of a material is inversely related to its volume.
Alumina ceramics are produced from fine particles that minimize the presence of voids in the material. Fewer voids contribute to higher density and volume. For instance, at 77°F (25°C), alumina ceramics have a density of 3.965 g/cm³ at standard atmospheric pressure. Higher density correlates with improved mechanical strength and wear resistance, making dense alumina ceramics desirable for demanding structural and engineering applications.
To achieve an optimal wear surface, manufacturers grind the alumina powder to a sub-micron (nanometer) level, resulting in a grain size of less than five microns after firing. Ceramic with 95% alumina content will have a grain size of 30 to 40 microns after firing, leading to larger voids and a higher wear rate. Conversely, ceramic with 87% alumina content will exhibit a grain size of three to five microns after firing, resulting in fewer voids and improved wear resistance. Fine-grained, high-density alumina ceramics are particularly sought after for precision components, electronic substrates, and biomedical implants where both surface smoothness and mechanical performance are critical.
The mechanical characteristics of a material are defined by its ability to withstand stress and strain. Alumina is noted for its exceptional strength and hardness, which increase with the purity of the various grades. Mechanical properties such as compressive strength, flexural strength, and fracture toughness define its performance in heavy-duty, load-bearing applications. Alumina ceramic components are widely used for wear plates, grinding media, bearings, and as substrate materials for electronic circuits, thanks to their durability and reliability in harsh conditions.
Thermal conductivity refers to a material's capacity to transfer heat. For instance, cooking pans need high thermal conductivity to cook food effectively. When a material is heated, its atoms vibrate more vigorously, causing their bonds to stretch. This phenomenon is described by the coefficient of thermal expansion. Due to their robust atomic bonds, alumina ceramics exhibit a low coefficient of thermal expansion, enhancing their stability under high temperatures.
Alumina ceramics possess high electrical resistivity, which minimizes thermal shock. Furthermore, higher purity forms of alumina have even greater resistivity. Superior thermal properties allow alumina to be used as thermal insulators, heat sinks, and protective sheaths in electrical and electronic assemblies, ensuring safe and sustained operation under extreme thermal cycling.
Alumina ceramics have exceptional dielectric properties compared to metals or plastic. Dielectric loss is a measurement of the amount of lost energy when a ceramic is subjected to electromagnetic voltage. With high conductivity, electrons move freely when exposed to electromagnetic voltage. The purpose of an insulator is to inhibit the flow of electrons. Alumina ceramics are able to withstand extreme exposure to electrical charges without any dielectric loss. This makes it a perfect insulation material because of its dielectric equality. Electric current is unable to pass through it.
As an electrical insulator, alumina ceramics are indispensable in manufacturing spark plug insulators, integrated circuit packages, power electronics, and microwave components, meeting demanding dielectric strength, insulation resistance, and reliability requirements in advanced technology sectors.
Hardness evaluates a material's capacity to resist mechanical wear and abrasion. Alumina ceramics surpass steel and tungsten carbide tools in hardness. On the Rockwell hardness scale, alumina ceramics range from HRA80-90, placing them just below diamonds and above stainless steel. This remarkable hardness supports applications including cutting tool inserts, ball bearings, armor plating, and dental prosthetics, where superior wear resistance and dimensional stability ensure long-term performance and reduced maintenance costs.
Alumina ceramics offer biocompatibility, making them suitable for use in medical and dental implants. Their non-magnetic nature allows deployment in sensitive electronic and MRI equipment, while their low outgassing and high purity enable usage in semiconductor processing and cleanroom environments. The versatility of advanced manufacturing methods—such as injection molding, isostatic pressing, and slip casting—further expand the design possibilities for custom alumina components tailored to unique industrial requirements.
When selecting alumina ceramics for your project, carefully consider application requirements such as chemical exposure, operating temperature, mechanical load, electrical insulation, and wear conditions. Consulting with expert alumina ceramic manufacturers and suppliers can help you identify the optimal composition, grade, and processing method to maximize performance and value in your specific industry—whether for electronics, aerospace, mining, energy, or biomedical technologies.
The raw material for alumina ceramics, or aluminum oxide ceramics, is derived from bauxite, an aluminum-rich, clay-like substance located just a few meters beneath the earth's surface. Bauxite mining is the initial stage in the alumina production process, enabling the extraction of this crucial raw material. The process of producing alumina—commonly known as the Bayer process—was developed in 1887 and remains the industry standard for generating high-purity alumina used in advanced ceramic applications.
After extraction, the bauxite ore is transported to a processing facility, where it is crushed and ground to obtain aluminum oxide (Al2O3). This purified aluminum oxide appears as a white, fine powder, which serves as the foundation for manufacturing technical ceramics, including high-performance alumina ceramic components employed across diverse industrial sectors such as electronics, medical devices, and aerospace.
The ground bauxite undergoes washing, drying, and blending with caustic soda (sodium hydroxide) and lime to create a slurry. This highly alkaline mixture is then heated in a digester to approximately 300°F (145°C) and maintained under 50 pounds of pressure for several hours. This step dissolves the aluminum-bearing compounds and separates them from residual impurities—including silica and iron oxide—essential for producing high-purity alumina suitable for electronic substrates and wear-resistant ceramic parts.
The heated slurry is transferred through a series of flash tanks to rapidly reduce pressure and temperature. These flash tanks facilitate the cooling process at atmospheric pressure, releasing steam while enabling the separation of dissolved aluminum compounds from the remaining solid residues.
Within settling tanks, insoluble impurities such as sand, iron, and other metals precipitate and settle at the bottom. The clarified liquid layer at the top undergoes filtration and multiple washes to recover dissolved alumina efficiently before progressing to the subsequent precipitation stage. This step is vital for creating ultra-pure alumina ceramics ideal for critical industrial and technical applications.
The filtered sodium aluminate solution is transferred into precipitators, where fine alumina particles are introduced as seeds to trigger the precipitation of aluminum hydroxide. Alumina crystallizes around these seeds, and the resulting particles settle to the bottom, forming a dense slurry. This precipitated alumina is subsequently processed in thickening tanks for further refinement and filtration, ensuring the highest levels of purity and particle size control for advanced ceramic manufacturing.
In the critical calcination phase, the aluminum hydroxide is heated in rotary or gas-fired inclined kilns to temperatures exceeding 1,000°C (1,832°F), effectively driving off water molecules and resulting in pure, anhydrous alumina powder. Additional filtration and washing steps eliminate any residual impurities and moisture. Modern fluid bed calcining technologies are increasingly adopted, where alumina particles are suspended above a hot air bed to achieve even heating. The outcome is a highly consistent, flowable alumina powder—the primary feedstock for fabricating dense, high-strength ceramic products, such as wear-resistant linings, electronic substrates, and biomaterial components.
These processing advancements in calcination enhance alumina purity and optimize particle size distribution to meet stringent quality standards in advanced engineering, thermal, and structural ceramic applications.
The resulting high-purity alumina powder is carefully blended with binders, plasticizers, and other additives according to the targeted alumina ceramic grade, such as 96%, 99%, or 99.9% alumina content. The specific formulation influences the ceramic's final physical properties, including mechanical strength, wear resistance, electrical insulation, and thermal conductivity. Common mixing approaches include spray dried powder, aqueous slip processing, and ceramic dough feedstock preparation.
Spray drying generates a granulated powder that is optimized for uniaxial and isostatic pressing techniques. The powder is mixed with a solvent, such as water or organic solutions, and a binder is incorporated prior to atomization, enhancing particle cohesion during pressing. This method is essential for producing dense, homogenous green bodies that are critical for high-precision technical ceramic parts.
In aqueous slip processing, alumina and any necessary additives are milled in water, accompanied by an organic dispersant, utilizing a ball mill. The resulting concentrated slurry, or slip, is ideal for slip casting and tape casting applications, which are commonly used to fabricate thin-walled ceramic components such as tubes, crucibles, and electronic substrates.
The ceramic dough feedstock technique involves blending water, high-purity alumina, a binder, and a plasticizer to achieve a plastic, moldable consistency. Achieving optimal consistency and green density is crucial for minimizing shrinkage and warping during subsequent firing or sintering processes, making this method well-suited for extrusion and injection molding applications.
Consolidation or forming refers to shaping the ceramic material into a “green body”—a preliminary form that can withstand handling and further processing. The choice of forming technique directly affects the mechanical strength, density, geometry, and overall quality of the finished alumina ceramic components. Common industrial consolidation methods include extrusion, uniaxial and isostatic pressing, electrophoretic deposition, and slip casting.
Injection molding of advanced ceramics involves mixing ultra-fine alumina powder with a polymeric binder system to produce a feedstock. This compound is then heated to yield a high-viscosity slurry, which is injected into complex-shaped molds to form the “green” ceramic part. Following molding, binders are thermally or chemically removed, and the green part is consolidated through high-temperature sintering or hot isostatic pressing. This process provides excellent geometry control, tight dimensional tolerances, and is used for complex-shaped technical ceramic products in industries such as medical, electronics, and automotive manufacturing.
Extrusion involves driving the ceramic dough feedstock through specially designed dies under high pressure. This technique creates continuous shapes with constant cross-sections (e.g., rods, tubes, channels) and is widely employed in the production of ceramic substrates, filtration elements, and structural parts. Binders and plasticizers play an important role in maintaining the integrity of the shaped part until it undergoes drying and thermal processing.
Isostatic pressing, which can be categorized as either wet or dry bag pressing, is vital for producing high-density, uniform ceramic bodies. During this process, spray-dried alumina powder is sealed in an elastomeric mold (usually made of rubber or polyurethane) and subjected to equal hydraulic pressure from all directions. Wet-bag pressing typically forms simple geometries, while dry-bag pressing can accommodate more complex ceramic parts. This method ensures minimized voids, improved mechanical properties, and isotropic density—critical for engineering ceramics used in high-wear and high-temperature environments.
Slip casting (or drain casting) is a time-tested forming technology in ceramic manufacturing. Concentrated aqueous slip—containing finely milled alumina and organic dispersants—is poured into a porous mold, usually made of plaster. Capillary action removes water from the slurry, depositing a solid ceramic layer on the mold’s interior. As thickness increases, excess slip is drained, and the molded part is dried before removal. Pressure casting is a related modern advancement that uses higher pressure to produce denser, thicker-walled green bodies, ideal for precision applications such as laboratory crucibles, insulators, and ceramic pipes.
Uniaxial (single-axis) pressing compacts alumina powder within a die using a top and bottom punch, typically operated by hydraulic or mechanical means. The process achieves green compacts of uniform density and is widely used to manufacture tiles, substrates, and other flat or simple geometric alumina ceramic shapes. The use of high-purity powder and well-coordinated binder systems is critical for minimizing defects and achieving desired strength in the finished product.
Electrophoretic deposition (EPD) is an innovative technology utilized within advanced ceramics manufacturing and industrial coatings. Alumina ceramic particles, suspended in a liquid medium, are attracted to an electrically charged mold, forming a tightly packed layer once the desired thickness is achieved. Following consolidation, the mold is removed or the excess suspension is drained, creating a green part ready for sintering. EPD allows for the uniform coating of complex geometries, making it popular in electronics and automotive ceramics for applications such as battery components and protective layers.
Sintering, also referred to as firing or densification, is the process of heating shaped green alumina bodies at temperatures typically between 1,600°C and 1,800°C. This results in densification and dramatically improves ceramic microstructure—crystallite grain growth, pore elimination, and enhanced mechanical performance. Solid-state sintering is the conventional approach for alumina ceramics and can result in up to 20% to 25% overall shrinkage, demanding precise control over the initial green body density and dimensions. Successful sintering results in a fully dense, high-strength ceramic part, well-suited for applications requiring electrical insulation, abrasion resistance, and thermal stability.
Machining operations on alumina can be performed at two critical stages: in the "green" (pre-sintered) state or after complete densification. Green machining allows for easier and faster shaping of intricate geometries using conventional cutting or drilling tools. However, due to significant shrinkage during sintering, final tolerances cannot be guaranteed, so secondary machining after sintering is usually required for precision applications. Post-sintering machining for alumina ceramics is typically executed with diamond-coated tools due to the material's exceptional hardness.
Diamond grinding is an essential finishing technique for alumina ceramics, performed post-sintering to achieve extremely tight dimensional tolerances, ultra-smooth surface finishes, and to remove any surface flaws. Techniques such as diamond cutting, honing, lapping, and polishing are employed, leveraging the superior hardness of both diamond abrasives and alumina ceramic material. This results in high-precision components ideal for biomedical implants, semiconductor manufacturing, and industrial wear parts.
Key Takeaways: The sophisticated production of alumina ceramics—from raw bauxite extraction and purification to advanced shaping and finishing processes—enables the creation of high-performance ceramic components that excel in demanding environments. Understanding these processing steps is critical for engineers, procurement professionals, and manufacturers who evaluate and specify alumina for use in electronics, automotive, aerospace, and industrial applications where superior wear resistance, electrical insulation, and mechanical strength are required.
The aim of alumina ceramics is to deliver components that exhibit high-temperature resistance, exceptional hardness, electrical insulation, and chemical inertness for various applications. Fortunately, several manufacturers have perfected their equipment for producing these ceramics. Below are five notable brands of machines used in the United States and Canada to produce alumina ceramics, including specific models and their unique features:
Features: CeraNova Corporation's High-Speed Ceramics Milling Machine is engineered for precise milling of alumina ceramics. It employs cutting-edge technology to achieve high material removal rates and superior surface finish. The machine includes options for high-speed spindles, multi-axis control, and specialized tooling for efficient ceramic machining.
Features: CoorsTek provides a variety of ceramic grinding media, including the alumina-based CeraSurf™. These media are suited for applications like ball and attritor milling. CeraSurf™ offers exceptional wear resistance, chemical inertness, and consistent particle size distribution, enhancing grinding efficiency and product quality.
Features: Sacmi USA Group's PH Series Presses are hydraulic machines tailored for alumina ceramic production. They offer precise control over pressure, speed, and stroke, enabling the creation of complex shapes with high density. The presses come with an intuitive interface, advanced automation features, and compatibility with downstream processes.
Features: Harper International's pusher furnaces are designed for the sintering of alumina ceramics. These furnaces provide controlled high-temperature atmospheres essential for sintering. They feature precise temperature control, uniform heating profiles, and adjustable residence times, supporting high throughput and various ceramic shapes and sizes.
Features: LECO Corporation's AMH43 Moisture Determination Analyzer is used for measuring moisture in alumina ceramics and other materials. It features a precision balance, high-temperature drying, and advanced software algorithms for accurate moisture content analysis. The analyzer offers rapid testing, ease of use, and customizable parameters.
Keep in mind that the availability and specifications of these models may change, so it is advisable to consult with the manufacturers for the most current information.
Alumina is a key engineering material known for its outstanding mechanical and electrical properties, making it suitable for a diverse array of applications. Some of its common uses are outlined below.
Alumina ceramics are widely used as insulation materials due to their excellent dielectric and thermal shock resistance. In high-frequency applications, extremely pure and dense alumina, fired at temperatures up to 1600°C, is utilized. This makes alumina ceramics essential for insulating components in television and satellite transmitter tubes, microwave generators, and lasers, where strength and durability are crucial.
Alumina ceramic labware is ideal for laboratory environments where high temperatures and contamination-free conditions are required. Its chemical and corrosion resistance, combined with high hardness, strength, durability, and wear resistance, makes alumina ceramics an excellent choice for various lab applications.
In the electronics industry, alumina ceramics are utilized for interconnectors, resistors, and capacitors. They serve as an economical and durable material for substrates in hybrid integrated circuits, surface mount devices, and sensors.
Alumina ceramic cutting tools are known for their strength and thermal conductivity. Previously costly, alumina cutting tools are now made more affordable through the use of composites and are produced by sintering and die pressing. These composites are commonly used as alternatives for abrasive and cutting tools, as well as in extrusions, nozzles, friction components in piston engines, and machinery where wear resistance is critical. Additionally, alumina ceramics are uniquely employed in the blades of Olympic ice skates.
Alumina ceramic is utilized in ballistics for its exceptional shock resistance, making it suitable for body armor in tanks, helicopters, and bulletproof vests. Alumina ceramics serve as the first line of defense against projectiles, designed to absorb the initial impact. After the alumina ceramic has absorbed this impact, a subsequent layer of material is used to dissipate the remaining kinetic energy, rendering the projectile inert.
Alumina ceramics are chemically inert, resistant to wear, and capable of achieving a highly polished finish, making them valuable as biomaterials. As a result, alumina ceramics are used in various medical applications, including artificial joints, bone spacers, cochlear implants, and dental implants. They are also employed in manufacturing tubes and scientific equipment. These advantageous properties make alumina ceramics an excellent choice for replacing body parts.
Alumina ceramic sheets offer versatile applications due to their resistance to extreme temperatures. Sheets with 99% alumina content are ideal for use in vacuum environments. Additionally, their machinability enables them to be shaped for use in harsh conditions, including high humidity environments
Since alumina ceramic sheets can withstand temperatures up to 2600 °F (1426 °C), the sheets are often used to make gaskets for furnaces and boilers and can be easily shaped using any form of cutting tool. The consistency and strength of alumina ceramic sheets varies depending on the percentage of alumina content. Thicknesses range from 0.01 in (0.0254 cm) up to 0.5 in (1.27 cm) and are available in various lengths and widths. These lengths and widths are limited by the size of the ovens available to finish them.
The grades and types of alumina ceramics are defined by their alumina content, which ranges from 70% to 99.9%. The specific percentage of alumina depends on the proportions of additional elements included in the mixture.
Alumina ceramics are characterized by their electrical properties, mechanical strength, wear resistance, chemical and corrosion resistance, and thermal stability, and they are dense and non-porous. These features make them suitable for applications such as electrical packaging, bushings, grinding media, wear-resistant components, and various industrial uses. For example, the tube lining shown below is composed of 92% alumina ceramics.
Has low thermal expansion, high volume resistivity, abrasion and chemical resistance, dielectric constant, and accepts manganese metal coating for high temperature brazing. It can be used as a pressure sensor, bearing coatings, electron tube, and laser components.
This grade offers similar characteristics to 94% alumina, with enhanced compressive and flexural strength, and excellent hermeticity. It is ideal for applications such as ceramic-to-metal feedthroughs, X-ray component feedthroughs, high-voltage bushings, and medical implants. Additionally, 95% alumina can be molded into body armor for military use.
Primarily used in medical applications, 96% alumina combines mechanical, electrical, thermal, and chemical properties. These attributes make it suitable for wear-resistant nozzles, guides, blood valves, electrical connector housings, and other industrial uses.
This grade can be metal-coated for high-temperature brazing assemblies and serves effectively as an electrical insulator. It is suitable for use in high-vacuum systems, laser equipment, X-ray tubes, electron microscopes, microwave windows, and insulation for medical devices.
97.5% alumina is a high-quality, fine-grain material used for electrical and mechanical components requiring thick metal coatings and high resistance to abrasion and chemicals. It is employed in metal-coated components such as conductor and resistor networks and dielectric layers, and is utilized in the defense industry, medical field, and scientific research.
This grade provides operational stability and reliability, maintaining electrical and dimensional stability across a wide temperature range. It is used in laser components, electro-optical devices, flow measurement instruments, sensors, and X-ray equipment.
98.6% alumina is a lightweight material used as armor for military vehicles and structures. It is capable of stopping small arms fire and medium-caliber projectiles.
99% alumina is extremely hard and is utilized in components for rotary and reciprocating pumps handling chemicals. It is used in shafts, bearings, thrust washers, plungers, and counterface seals in chemical pumps.
99.5% alumina is a highly pure form of alumina used in semiconductor applications, including chambers and fixtures. It features low particle generation and is vacuum-tight.
This grade has a 98% reflectance efficiency at 1064 nanometers (nm) and a 96% reflectance at wavelengths from 500 to 2000 nm, making it ideal for laser reflectors. It is suitable for use in pumping chambers for flash lamps and continuous wave lasers.
99.8% alumina is extremely pure and developed for semiconductor applications. It offers excellent chemical and plasma resistance with high dielectric properties for high-voltage applications. It is used in various semiconductor processes, including PVD, CVD, CMP oxide etching, ion implantation, and photolithography, among others.
99.9% alumina is an ultra-pure form suitable for severe applications such as plasma etching components and nuclear-grade insulators. The properties of 99.9% alumina are detailed in the chart below from CoorsTek.
| Property | Units | Value |
| Flexural Strength, MOR (20 °C) | MPa | 350 - 600 |
| Fracture Toughness, KIc | MPa m1/2 | 4.0 - 5.0 |
| Thermal Conductivity (20 °C) | W/m K | 28 - 35 |
| Coefficient of Thermal Expansion | 1 x 10-6/°C | 8.0 - 8.5 |
| Maximum Use Temperature | °C | 1750 - 1800 |
| Dielectric Strength (6.35mm) | ac-kV/mm | 8.7 |
| Dielectric Loss (tan δ) | 1MHz, 25 °C | 10-4 to 10-3 |
| Volume Resistivity (25°C) | Ω-ł¦łľ | 1014 to > 1015 |
Zirconia toughened alumina is produced by combining aluminum oxide with 10% to 20% zirconium oxide. The resulting material has exceptional strength, toughness, hardness, and outstanding wear resistance. It provides a design solution that is less expensive than using zirconia alone, which can cost anywhere from $75 to $400 per carat. The cost of zirconia varies in accordance with its purity and quality.
The process of combining alumina oxide with zirconia oxide enhances the fracture toughness of Zirconia Toughened Alumina (ZTA). When zirconia is subjected to stress, its crystal structure transforms, leading to a volume expansion that compresses any cracks within the alumina matrix. This transformation significantly increases the structural strength of alumina, making it suitable for a wide range of demanding applications.
A ceramic insulator is a non-conductive insulator made from red, brown, or white porous clay that provides a bridge between electronic components and has high dielectric strength and constant and low electrical loss. They are easy to maintain and...
Ceramic machining refers to the manufacture of ceramic materials into finished usable products. Machining involves the continual removal of material from the workpiece, in this case, ceramic material...
Zirconia Ceramics, or zirconium dioxide ceramics, are exceptionally strong technical ceramic materials with excellent hardness, toughness, and corrosion resistance without the brittleness common to other ceramic materials...
Acid etching, also known as chemical etching or photo etching, is the process of cutting a hard surface like metal by means of a specially formulated acid for the process of etching in order to allow for the creation of a design onto the metal...
Chemical milling is a subtractive machining process that removes material from a workpiece to achieve a desired shape. Unlike aggressive milling methods that depend on sharp tools to produce a design, chemical...
Glass cutting is a method of weakening the structure of glass along a score line that can be broken by applying controlled force; this separates the glass into two sections along the score line or fissure. Regardless of the application, the cutting of glass is...
Metal etching is a metal removal process that uses various methods to configure complex, intricate, and highly accurate components and shapes. Its flexibility allows for instantaneous changes during processing...
Photochemical etching, also known as photochemical machining or metal etching, is a non-traditional, subtractive machining process in which photographic and chemical techniques are used to shape the metal workpiece...
Quartz is one of the most abundant and widely distributed minerals in nature. Quartz is the only stable polymorph of crystalline silica on the Earth‘s surface. It is found in all forms of rocks: igneous, metamorphic and sedimentary. It becomes concentrated in...